Commonly used intaglio printing inks, after being stored for a long time, will cause the ink to dry due to the volatilization of the solvent, resulting in the inability of the ink to be used. If diluted with this agent, dry ink can be regenerated. In addition, when preparing a gravure printing ink, if the ink is too dry, it can be diluted with this agent.
1. Features and uses
This agent is made by mixing and dissolving resin and solvent. It has good compatibility with gravure printing ink, does not reduce the adhesion strength of ink on ethylene film, is easy to obtain raw materials, and is simple to prepare.
This agent is dedicated to dilute intaglio printing inks.
2. Raw Materials (1) Vinyl chloride-vinyl acetate copolymer White or light blue powder. Non-toxic, odorless. Soluble in acetone, cyclohexanone, chlorinated hydrocarbons, soluble in dichloroethane, insoluble in water, alcohol, chain hydrocarbons, concentrated acid, concentrated alkali. It swells in aromatics, ethers, and esters. This agent is one of the main raw materials. Use industrial products.
Production plants: Beijing No. 2 Chemical Plant, Shanghai Tianyuan Chemical Plant, Jiangsu Xuzhou Electrochemical Plant, Sichuan Yibin Chemical Plant.
(2) Polyvinyl Chloride Resins See section XIV (IV) Non-flammable polyvinyl chloride sheets. This agent is one of the main raw materials. Use industrial products.
(3) Cyclohexanone See (viii) Epoxy resin anti-corrosion coating. This agent is used as a solvent. Use industrial products.
(4) Xylene See the fifth (9) multifunctional paint remover. This agent is used as a solvent. Use industrial products.
(5) Butyl acetate See the sixteenth (five) advanced and colorful gravure printing inks. This agent is used as a solvent. Use industrial products.
3. Formula vinyl chloride-vinyl acetate copolymer 250g
PVC resin 250g
Cyclohexanone 2000mL
Xylene 2000mL
Butyl acetate 1000mL
PVC resin 250g
Cyclohexanone 2000mL
Xylene 2000mL
Butyl acetate 1000mL
Small preparation and use method According to the formula volume requirements, vinyl chloride-vinyl acetate and polyvinyl chloride resin are dissolved in a mixed solvent consisting of cyclohexanone, xylene and butyl acetate, and the mixture is stirred to completely dissolve the resin. If you add a small amount of acetone properly, you can speed up the drying rate.
When used, add the dilute ink to be diluted, mix and brewed evenly.
1. Features and uses
This agent is made by mixing and dissolving resin and solvent. It has good compatibility with gravure printing ink, does not reduce the adhesion strength of ink on ethylene film, is easy to obtain raw materials, and is simple to prepare.
This agent is dedicated to dilute intaglio printing inks.
2. Raw Materials (1) Vinyl chloride-vinyl acetate copolymer White or light blue powder. Non-toxic, odorless. Soluble in acetone, cyclohexanone, chlorinated hydrocarbons, soluble in dichloroethane, insoluble in water, alcohol, chain hydrocarbons, concentrated acid, concentrated alkali. It swells in aromatics, ethers, and esters. This agent is one of the main raw materials. Use industrial products.
Production plants: Beijing No. 2 Chemical Plant, Shanghai Tianyuan Chemical Plant, Jiangsu Xuzhou Electrochemical Plant, Sichuan Yibin Chemical Plant.
(2) Polyvinyl Chloride Resins See section XIV (IV) Non-flammable polyvinyl chloride sheets. This agent is one of the main raw materials. Use industrial products.
(3) Cyclohexanone See (viii) Epoxy resin anti-corrosion coating. This agent is used as a solvent. Use industrial products.
(4) Xylene See the fifth (9) multifunctional paint remover. This agent is used as a solvent. Use industrial products.
(5) Butyl acetate See the sixteenth (five) advanced and colorful gravure printing inks. This agent is used as a solvent. Use industrial products.
3. Formula vinyl chloride-vinyl acetate copolymer 250g
PVC resin 250g
Cyclohexanone 2000mL
Xylene 2000mL
Butyl acetate 1000mL
PVC resin 250g
Cyclohexanone 2000mL
Xylene 2000mL
Butyl acetate 1000mL
Small preparation and use method According to the formula volume requirements, vinyl chloride-vinyl acetate and polyvinyl chloride resin are dissolved in a mixed solvent consisting of cyclohexanone, xylene and butyl acetate, and the mixture is stirred to completely dissolve the resin. If you add a small amount of acetone properly, you can speed up the drying rate.
When used, add the dilute ink to be diluted, mix and brewed evenly.